The team concluded that the pipeline had failed due to a fatigue crack that had grown to a critical size. The crack had formed in the weld region, which had a lower toughness than the base metal.

K = 85 MPa√m < KIC = 100 MPa√m

The team also discovered that the pipeline had been subjected to a series of pressure cycles, with pressures ranging from 500 to 900 psi. These cycles had caused fatigue cracks to form and grow in the weld region. principles of fracture mechanics rj sanford pdf pdf work

K = (900 psi * √(π * 2 inches)) * 1.5 = 85 MPa√m The team concluded that the pipeline had failed

where Y is a geometric factor that depends on the crack configuration and the component geometry. principles of fracture mechanics rj sanford pdf pdf work